Recharging on Stable, Amorphous Silicon
October 11, 2016 | WileyEstimated reading time: 1 minute
Next-generation anodes for lithium ion batteries will probably no longer be made of graphite. Silicon, which is a related material, can provide a much higher capacity than graphite, but its crystallinity poses problems. In the journal Angewandte Chemie ("Mesoporous Amorphous Silicon: A Simple Synthesis of a High-Rate and Long-Life Anode Material for Lithium-Ion Batteries"), Chinese scientists have introduced a porous silicon form that is amorphous, not crystalline, and has the potential to outstrip the other materials in rechargeable battery applications.
Although carbon in its graphite form is the most common anode material today in lithium ion batteries, its capacity is relatively low. Other long-standing issues of lithium ion batteries are poor cycle life, increasing internal resistance with cycling, ageing, and safety concerns. Silicon offers a theoretical capacity almost ten times higher than that of graphite.
However, silicon does not like cycling: Its crystalline structure expands and shrinks with every charge-discharge cycle, which leads to pulverization and capacity loss. Jian Yang and his team at Shangdong University in China have now a prepared a porous amorphous silicon modification that compensates for the disadvantages.
Yang said that investigation of the amorphous state was the logical consequence because silicon would loose crystallinity anyway. The authors wrote: "As silicon eventually becomes amorphous during electrochemical lithiation/delithiation, the attempt to use amorphous silicon ... from the beginning draws intense interest."
On the other hand, amorphous silicon structures are rather difficult to prepare and the preparation conditions have to be carefully chosen. The scientists eventually came up with a relatively simple process, using safe substances as the starting materials, as they pointed out. For example, they used cheap and common glyme as the solvent, and liquid silicon tetrachoride as the silicon precursor, which would be easier to handle than other substances. All this makes their procedure "very attractive for the mass production," as they put it.
The resulting porous amorphous silicon material exhibited excellent electrochemical characteristics with a capacity three times better than graphite, and much longer cycling stability than crystalline silicon. Yang and his colleagues explained this stability by the presence of large, solvent-filled pores in the material and by the partial oxidation of the silicon surface in air. And there is more potential for the future. Yang proposes that a pinch of carbon in the structure would even further enhance its electrochemical performance.
Suggested Items
RTX Signs Largest Renewable Electricity Deal with ENGIE
04/19/2024 | RTXRTX announced an agreement with a subsidiary of ENGIE North America (ENGIE) that will provide 100% renewable electricity to 12 of the company’s Texas facilities.
RTX Provides Blue Canyon Satellite to Help Solve a Crucial Climate Challenge
04/16/2024 | RTXBlue Canyon Technologies, RTX's small satellite manufacturer and mission services provider, announced the successful launch and initial contact with the MethaneSAT satellite.
Report Reveals ‘True Impact’ of Manufacturing is Nearly a Quarter of UK GDP
04/15/2024 | Manufacturing Technologies AssociationManufacturing is having a far greater impact on the UK economy than first thought according to a major new report released today.
IDC Estimates that GenAI Will Increase Marketing Productivity More Than 40% by 2029
04/03/2024 | IDCNew research from International Data Corporation (IDC) shows that applying generative artificial intelligence (GenAI) to a range of enterprise marketing tasks will result in an estimated productivity increase of more than 40% by 2029.
North American PCB Industry Sales Down 11.6% in February
03/25/2024 | IPCIPC announced today the February 2024 findings from its North American Printed Circuit Board (PCB) Statistical Program. The book-to-bill ratio stands at 1.07.